NANTAI NVERSTES MATERIALS SCIENCE CHAPTER 5 SOLIDIFICATION AND

NİŞANTAŞI ÜNİVERSİTESİ MATERIALS SCIENCE CHAPTER 5 - SOLIDIFICATION AND PHASE DIAGRAMS Mühendislik Mimarlık Fakültesi mmf. nisantasi. edu. tr NİŞANTAŞI ÜNİVERS İTESİ ©

SOLUBILITY • Complete Solubility: Infinite solubility of an element in another element. • Non-solubility: Non-solubility of an element in another element. • Limited Solubility: Limited solubility of an element in another element. a) b) c)

Limited Solubility • Often observed in alloy systems. • B element can be solved in A element only in a limit • The solubility is= At room temperature, X 1 percent; as temperature rises such as at eutectic temperature, X 2 percent • As temperature rises, thermal activation increases and thus the amount of holes increases.

• Samely, element A can be solved in element B in a limit. • The solubility is= At room temperature, X 3 percent; as temperature rises such as at eutectic temperature, X 4 percent

fazı: Katı Çözelti • Foreign atoms which cannot be incorporated in the solution, form a new phase. This phase is rich in these foreign atoms. • Solid solution which is rich in A, form phase. • Solid solution which is rich in B, form phase. • Physically and chemically different two phases, and can co-exist in the microstructure. fazı: 2. Faz ve Katı çözelti

EUTECTOID REACTION • Soğuma sırasında bir katı fazdan iki ayrı katı fazın oluşması reaksiyonudur. Ötektoid reaksiyon: (Katı) Soğuma (Katı) + (Katı)

PERITECTIC REACTION • Kısmi çözünürlük gösteren alaşım sistemlerinde elementlerin ergime sıcaklıklarının çok farklı olması durumunda meydana gelen faz reaksiyonlarıdır. Peritektik reaksiyon: Sıvı + (Katı) Soğuma (Katı)

IRON-CARBON PHASE DIAGRAM +S (ostenit) S +S Sementit : Fe 3 C Ferrit : Perlit : + Fe 3 C Ostenit: Delta demir: Ledeburit. Tötektik Perlit Ledeburit 1148 o. C Çelik Dökme demir %C: ağırlık olarak Tötektoid

REFERENCES 1. The Science and Engineering of Materials, 4 th ed Donald R. Askeland – Pradeep P. Phulé NİŞANTAŞI ÜNİVERSİTESİ ©