Observe nanoscale structure by scattering SANS Guinier regime

Observe nano-scale structure by scattering SANS基本原理 双相体系 Guinier regime: gyration radius Scattering laws 对纳米颗粒体系（弥散分布的纳米不均匀结构） 衬度 单个颗 粒形状 颗粒间 关联 Intermediate regime: shape and dimensions I(q)q→ 0: Vp (or mass） Porod regime: specific surface S/V of the sample. 散裂中子源进展汇报 26 November 2020 Page 3

~4 m+4 m R CSNS SANS介绍 R 1 R 2 关键部件构成 Collimation: L 1= to 11. 8 m, L 2=2 to 4 m； Q=4πsin(θ)/λ ; λ =0. 5 to 12 A by TOF 入射中子波� Q� 范� 0. 5~12Å Qmin < 0. 01Å-1 Qmax > 1Å-1 Q分辨率 中子通量(� 品位置) 散裂中子源进展汇报 26 November 2020 ~50% for Qmin 106 n/cm 2/s 探� 器分辨率 8 mm (3 He LPSD) 探� 器有效探� 面� 1 m 2 � 品大小 8~12 mm Page

2. 谱仪调试 作总结_标样实验 Silver behenate （粉体） d(001) = 58. 38Å —Debye ring at 0. 11Å-1 首次测 试数据 CAEP SANS 数据 探测器初步刻度——衍射环变圆 Neutron Scattering on Polyethylene 散裂中子源进展汇报 26 November 2020 2. 8 A_25 mm 2. 8 A_50 mm Page