Chap 12 Fundamentals of Metal Forming n Chap

Chap. 12 Fundamentals of Metal Forming (성형) n 산업시스템공학과 제조자원 강의

Chap. 13 Hot Working Processes n Bulk deformation : -재료의 표면적이 많이 변화 Thickness, cross-sec tion이 축소 -volume은 constant로 일정 -shape이 complex한 형상

Hot Working Processes n Sheet-Forming : thickness, surface area는 상당히 constant n Hot working process : Rolling, Forging, Extrusion, Hot drawing, Pipe welding, Piercing(찔러 구멍내기)

Hot Working Processes n n 13. 4 Rolling see Fig 13. 1 abundance of rolling operation

Hot Working Processes n see Fig 13. 2

Hot Working Processes n see Fig 13. 3 reversing/non-reversing

Hot Working Processes n see Fig 13. 5

Hot Working Processes n see Fig 13. 6

Hot Working Processes n n 13. 5 Forging see Fig 13 -9 Basic tooling open die drop hammer forging(대장간)

Hot Working Processes n see Fig 13 -10, impression-die forging (형다이 단조)

Hot Working Processes n see Fig 13 -11

Hot Working Processes n see Fig 13 -12 flash는 trimming die에서 절단 , 대량생산가능

Hot Working Processes n see Fig 13 -13 impactor metal flow

Hot Working Processes Upset forging upset forging rule ⅰ) unsupported metal의 길이 ≤ 3 d(bar stock) ⅱ) upset 길이가 3 d이상일 경우 cavity diameter ≤ 1. 5 d(bar stock) ⅲ) upset 길이가 3 d 이상이고 upset diameter 가 1. 5 d(bar stock)일 경우 die 사이의 공간 이 ≤d 이하

Hot Working Processes n see Fig 13 -16

Hot Working Processes n Fig 13 -18 n (b) production rate : 90 -180 part/min by automatic hot forging n

Hot Working Processes n n n Net-shape or Near Net-shape Forging gear의 forging에서 원가의 80%는 마무리 기계 가공비 비행기 날개 의 spar(돛대, 장대)는 재료의 96%를 scrap으로 낭비하고 단 4%만 사용 final dimension으로 정확히 forging 하면 재료비 절감, 원가절감 → Near Net-shape forging Cost saving은 기계가공의 제거, (handling, positioning, fixturing), scrap제거, 에너지 축소 draft angle, 1°

Hot Working Processes n 13. 6 Extrusion Fig 13 -22

Hot Working Processes n Fig 13 -23 Typical shapes

Hot Working Processes n n direct extrusion indirect extrusion Fig 13 -24, Fig 13 -25

Hot Working Processes n Fig 13 -26