Carbon Fiber Composite Material Specification InHousing Processing Prepreg
Carbon Fiber Composite Material Specification In-Housing Processing & Prepreg Processing
In- House Processing Bulk -6 mm Bulk -13 mm Bulk -37 mm Prepreg -Standard Pregreg- HT Tensile Strength (MPa) 273 301 468 612 490 Tensile Modulus 21 24 28 35 30 Flexural Strength (MPa) 324 365 490 630 533 Flexural Modulus 22 25 30 48 32 42 43 45 50 48 1. 3 1. 4 1. 5 -67/300 -67/300 Tg (˚F) 350 350 350 Characters 6 mm chopped CF 13 mm chopped CF 37 mm chopped CF Standard Prepreg High Temperature Application Mechanical Properties (GPa) Shear Strength (MPa) Physical Properties Density (g/cc) Operating Temp (˚F)
CF Prepreg Processing 1101 106/8 301 304 -1 350 4565 307 316 2510 8552 Mechanical Properties Tensile Strength (MPa) 745 441 710 586 772 860 780 972 912 765 23 68 62 83 90 85 79. 3 55. 8 65 Flexural Strength 682 (MPa) 593 830 793 689 750 802 1210 709 958 Flexural Modulus 52. 4 24 50 51 69 73 70 75. 1 54. 9 60 50 73 64 61 63 97. 9 97. 2 60 110 1. 55 1. 57 1. 55 1. 53 1. 58 -67/200 -67/180 -67/200 -67/350 -67/450 -67/200 Tg (˚F) 230 252 248 377 239 316 294 392 Characters General Purpose Flame Retardant Toughened System Impact Resistance High Temperature Application Design for high thickness Flame retardant designed for electrical applications. Aerospace primary Damage Tolerance Tensile Modulus 53. 8 (GPa) Shear Strength 56. 5 (MPa) Physical Properties Density (g/cc) Operating Temp (˚F) 700 Extra High Tg
- Slides: 3